5083 Aluminum Plate
5083 aluminum is the most widely used anti-rust aluminum. This alloy has high strength, especially fatigue resistance: high plasticity and corrosion resistance. It cannot be strengthened by heat treatment. It has good plasticity during semi-cold work hardening and cold work. Because the material is a high-magnesium alloy, it has good strength, corrosion resistance, and machinability among non-heat-treatable alloys. The surface is beautiful after anodizing. Arc welding performance is good. The main alloying element in 5083 alloy is magnesium, which has good corrosion resistance and weldability, as well as medium strength. Excellent corrosion resistance makes 5083 alloy widely used in maritime applications such as ships, as well as automobiles, aircraft welding parts, subways and light rails, and pressure vessels that require strict fire protection.
Product Parameters
| Width | 20-3000mm or Customized | Thickness | 0.1-120mm or Customized |
| Length | 100-12000mm or Customized | Certificate | ISO, SGS, BV |
| Standard | JIS, AISI, ASTM, GB, DIN, EN, etc. | ||
| Brand | 1000 Series: 1050, 1060, 1070, 1100, 1200, 1235, etc. | ||
| 3000Series: 3003, 3004, 3005, 3104, 3105, 3A21, etc. | |||
| 5000 Series: 5005, 5052, 5083, 5086, 5154, 5182, 5251, 5754, 5A05, etc. | |||
| 6000 Series: 6061, 6063, 6082, 6A02, etc. | |||
| 7000 Series: 7050, 7475, 7075, etc. | |||
| 8000 Series: 8A06, 8011, 8090, etc. | |||
| Surface | Coating, Embossing, Drawing, Polishing, Anodizing, etc. | ||
| OEM Service | Punching, Cutting Special Size, Making Flat Surface, Surface Treatment, etc. | ||
| Delivery Time | Received 30%, After deposit 7-15 working day | ||
| Application | Construction, Shipbuilding, Decoration, Industry, Manufacturing, Machinery, Hardware And Other Fields, etc. | ||
| Sample | Free Offers Sample | ||
| Packaging | Strapping, plastic bag, film, wooden pallet Standard seaworthy export packing or according to customer requirement | ||
Mechanical Properties
| Tensile Strength (MPa) |
Yield Strength (MPa) |
Elongation Rate (%) |
Hardness (HV) |
| 290 | 145 | 22 | 87 |