1050 Aluminum Plate
Aluminum 1050 alloy is usually based on 99.5% pure aluminum, adding an appropriate amount of copper, manganese, magnesium and other elements for smelting. The density of aluminum 1050 alloy is about 2.7g/cm, which is lighter than traditional materials such as steel, helping to reduce product weight and improve energy efficiency. Besides, aluminum 1050 alloy has high strength and good fatigue resistance, which can improve the service life of 1050 aluminum plate. Aluminum 1050 alloy also has excellent electrical and thermal conductivity, which contributes to the heat dissipation and energy transmission of the product. Moreover, 1050 aluminum plates can resist the corrosion of acid, alkali, salt and other corrosive media to a certain extent. Aluminum 1050 alloy is easy to process, and can be made into various profiles, plates, pipes and so on by rolling, extrusion, stretching and other methods.
Product Parameters
| Width | 20-3000mm or Customized | Thickness | 0.1-120mm or Customized |
| Length | 100-12000mm or Customized | Certificate | ISO, SGS, BV |
| Standard | JIS, AISI, ASTM, GB, DIN, EN, etc. | ||
| Brand | 1000 Series: 1050, 1060, 1070, 1100, 1200, 1235, etc. 3000Series: 3003, 3004, 3005, 3104, 3105, 3A21, etc. 5000 Series: 5005, 5052, 5083, 5086, 5154, 5182, 5251, 5754, 5A05, etc. 6000 Series: 6061, 6063, 6082, 6A02, etc. 7000 Series: 7050, 7475, 7075, etc. 8000 Series: 8A06, 8011, 8090, etc. |
||
| Surface | Coating, Embossing, Drawing, Polishing, Anodizing, etc. | ||
| OEM Service | Punching, Cutting Special Size, Making Flat Surface, Surface Treatment, etc. | ||
| Delivery Time | Received 30%, After deposit 7-15 working day | ||
| Application | Construction, Shipbuilding, Decoration, Industry, Manufacturing, Machinery, Hardware And Other Fields, etc. | ||
| Sample | Free Offers Sample | ||
| Packaging | Strapping, plastic bag, film, wooden pallet Standard seaworthy export packing or according to customer requirement | ||
Chemical Composition
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others: | Others: | Al: Min. |
| Each | Total | ||||||||||
| 1050 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | – | 0.05 | 0.03 | 0.03 | – | 99.5 |
| 1060 | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | – | 0.05 | 0.03 | 0.03 | – | 99.6 |
| 1070 | 0.2 | 0.25 | 0.04 | 0.03 | 0.03 | – | 0.04 | 0.03 | 0.05 | – | 99.7 |
| 1100 | 0.95 Si Fee | 0.05~0.20 | 0.05 | – | – | 0.1 | – | 0.05 | 0.15 | 99 | |
| 2014 | 0.5~1.2 | 0.7 | 3.9~5.0 | 0.4~1.2 | 0.2~0.8 | 0.1 | 0.25 | 0.15 | 0.05 | 0.15 | Margin |
| 2017 | 0.2~0.8 | 0.7 | 3.5~4.5 | 0.4~1.0 | 0.4~0.8 | 0.1 | 0.25 | 0.15 | 0.05 | 0.15 | 91.5 – 95.5 |
| 2024 | 0.5 | 0.5 | 3.8~4.9 | 0.3~0.9 | 1.2~1.8 | 0.1 | 0.25 | 0.15 | 0.05 | 0.15 | Margin |
| 3003 | 0.6 | 0.7 | 0.05~0.20 | 1.0~1.5 | – | – | 0.1 | – | 0.05 | 0.15 | Margin |
| 3A21 | 0.6 | 0.7 | 0.2 | 1.0-1.6 | 0.05 | – | 0.15 | 0.1-0.2 | – | – | Margin |
| 3004 | 0.3 | 0.7 | 0.25 | 1.0~1.5 | 0.8~1.3 | – | 0.25 | – | 0.05 | 0.15 | Margin |
| 3005 | 0.6 | 0.7 | 0.3 | 1.0~1.5 | 0.2~0.6 | 0.1 | 0.25 | 0.1 | 0.05 | 0.15 | Margin |
| 3105 | 0.6 | 0.7 | 0.3 | 0.3~0.8 | 0.2~0.8 | 0.2 | 0.4 | 0.1 | 0.05 | 0.15 | Margin |
| 5005 | 0.3 | 0.7 | 0.2 | 0.2 | 0.5~1.1 | 0.1 | 0.25 | – | 0.05 | 0.15 | Margin |
| 5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2~2.8 | 0.15~0.35 | 0.1 | – | 0.05 | 0.15 | Margin |
| 5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6~3.6 | 0.3 | 0.2 | 0.15 | 0.05 | 0.15 | Margin |
| 5A05 | 0.5 | 0.5 | 0.1 | 0.3-0.6 | 4.8-5.5 | – | 0.2 | – | 0.05 | 0.05 | Margin |
| 5083 | 0.4 | 0.4 | 0.1 | 0.4~1.0 | 4.0~4.9 | 0.05~0.25 | 0.25 | 0.15 | 0.05 | 0.15 | Margin |
| 6061 | 0.40~0.8 | 0.7 | 0.15~0.4 | 0.15 | 0.8~1.2 | 0.04~0.35 | 0.25 | 0.15 | 0.05 | 0.15 | Margin |
| 6082 | 0.70~1.3 | 0.5 | 0.1 | 0.4~1.0 | 0.6~1.2 | 0.25 | 0.2 | 0.1 | 0.05 | 0.15 | Margin |
| 7075 | 0.4 | 0.5 | 1.2~2.0 | 0.3 | 2.1~2.9 | 0.18~0.28 | 5.1~6.1 | 0.2 | 0.05 | 0.15 | Margin |
Mechanical Properties
| Tensile Strength | Test Stress | Hardness | Elongation Rate |
| (MPa) | 0.2% (MPa) | HB | (%) |
| 105-145 | ≥85 | ≥34 | ≥12 |
Physical Performance
| Density | Melting Point | Modulus of Elasticity | Thermal Conductivity | Thermal Expansion | Resistivity |
| 2.71Kg/m³ | 650°C | 71GPa | 222 W/m.K | 24×10-6/K | 0.282 × 10-6Ω.m |
Annealing State
| Brand | Annealing State |
| 1xxx: 1050, 1050A, 1060, 1100 | O, H12, H14, H16, H18, H22, H24, H26, H28, H111 |
| 3xxx: 3003, 3004, 3005, 3105 | |
| 5xxx: 5005, 5052, 5754, 5083, 5086, 5182, 5049, 5251, 5454 | O, H22, H24, H26, H28, H32, H34, H36, H38, H111 |
| 6xxx: 6061, 6082 | T4, T6, T451, T651 |
| 2xxx: 2024 | T3, T351, T4 |
| 7xxx: 7075 | T6, T651 |
Scope of Application
| Aluminum Uses And Application Area | |
| Food Packaging | Beverage can ends, cans, bottle caps, etc. |
| Building | Curtain walls, cladding, suspended ceilings, thermal insulation, venetian blinds, etc. |
| Transportation | Auto parts, passenger car bodies, aviation ships and air cargo containers. |
| Electronic Equipment | Electrical appliances, communication equipment,PCPlate drilling guide, lighting and heat dissipation materials, etc. |
| Consumer Goods | Umbrellas, cooking utensils, sports equipment, etc |
| Other | Military, color coated aluminum plate, etc. |